GREEN PLASTIC LUMBER COMPOSITION BY WEIGHT

Minimum, RECYCLED POLYETHYLENE:

HDPE = 40%

Minimum, RECYCLED POLYETHYLENE:

LDPE = 30%

Minimum, RECYCLED POLYPROPYLENE:

PP = 30%

Additives to ensure U.V. Stabilization and Flame Retrardency may total no more than 2%.

PROPERTY TEST Measurement Results

Abrasion Test ASTM D4060 0.42 grms – weight loss

Abrasion Test (Taber tester CS 17 1.01 in³ (16.55 Cu cm)

100 Hrs.)

Absorption (Diesel Fuel) ASTM D543 0.677 % Weight Increase

Absorption (Gasoline) ASTM D543 1.362 % Weight Increase

Absorption (Sea Water) ASTM D543 0.116 % Weight Increase

Brittleness ASTM D746 No Break @ -40ºC @ 267m-N/m

Bulk Density ASTM D6111 60.12 lb/ft³ (963 Kg/cu m)

Coefficient of Friction

(Neolite-wet) ASTM C1028 0.50

Coefficient of Friction ASTM C1028 0.55

(Neolite-dry)

Coefficient of Thermal ASTM D696 0.000076 in/in/ºF

Expansion

Compressive Strength

Compression Strength ASTM D6108 1,960 psi (13.5 Mpa)

Parallel to Grain ASTM D6112 3,560 psi (24.6 Mpa)

Compression Strength ASTM D6112 1,180 psi (8.1 Mpa)

Perpendicular to Grain

Flammability (Flash Point) GREEN PLASTIC LUMBER 660 ºF (350ºC)

Flexural Creep Rupture (Fiber

Stress) ASTM D6112 383 psi (2.6 Mpa)

Flexural Creep Rupture (Max ASTM D6112 0.76 %

Stress %)

Flexural Strength ASTM D790 @ 5” deflection 2,060 psi (14.1 Mpa)

Flexural Strength ASTM D6109 no fracture @ 2,500 psi (17.2 Mpa)

Hardness ASTM D2240 72 Shore D

Impact Resistance ASTM D746 325 m-N/m

IZOD Impact ASTM D256 4.54 lb.ft./in.

Melting Point GREEN PLASTIC LUMBER Melt 271ºF (133&degC), Soften 261ºF

(127ºC)

330,400 psi (2,278.6 Mpa)

Modulus of Elasticity ASTM D198 10” = 603,500 psi (4,162 Mpa)

Modulus of Elasticity ASTM D638 3” = 340,900 psi (2,407 Mpa)

Modulus of Elasticity ASTM D6109 10”= 332,500 psi (2,293 Mpa)

Modulus of Rupture ASTM D198 2,480 psi (17.1 Mpa)

Nail Withdrawal (Surface) ASTM D6117 281 lbs., (104 Kg)

Screw Withdrawal (Surface) ASTM D6117 490 lbs., (183 Kg)

Shear Parallel to Length ASTM D143 986 psi (6.8 Mpa)

Specific Gravity ASTM D6111 0.965

Tensile Strength ASTM D638 3,060,psi (21.1 Mpa)

UV Resistance (Skin) ASTM D4329 1% Change after 500 hrs.